Matrimid-JUC-62 and Matrimid-PCN-250 mixed matrix membranes displaying light-responsive gas separation and beneficial ageing characteristics for CO2/N2 separation

Abstract

The performance of two generation-3 light-responsive metal-organic framework (MOF), namely JUC-62 and PCN-250, was investigated in a mixed matrix membrane (MMM) form. Both of them were incorporated inside the matrimid as the polymer matrix. Using our custom-designed membrane testing cell, it was observed that the MMMs showed up to 9% difference in CO2 permeability between its pristine and UV-irradiated condition. This shows that the light-responsive ability of the light-responsive MOFs could still be maintained. Thus, this finding is applicable in designing a smart material. Apart from that, the MMMs also has the potential to be applied for post-combustion carbon capture. At loadings up to 15 wt%, both CO2 permeability and CO2/N2 ideal selectivity could be significantly improved and surpassed the value exhibited by most of the MOF-matrimid MMM. Lastly the long term performance of the MMM was also evaluated and it was observed that both MMM could maintain their performance up to 1 month with only a slight decrease in CO2 permeability observed for 10 wt% PCN-250-matrimid. This study then opens up the possibility to fabricate a novel anti-aging multifunctional membrane material that is applicable as a smart material and also in post combustion carbon capture applications. © 2018 The Author(s).

Publication
Scientific Reports